IMPORTANT WARNINGS
Failure to follow warnings and instructions can result in serious injury or death.
Refer to warnings
These warnings also apply to cordage (rope). Only additional warnings and information are listed below.
Never exceed the Working Load Limit of rope.
Use Working Load Limits as published as guidelines only. Working Load Limit may have to be reduced when life, limb or valuable property are at risk, or other than new rope is used. When using multiple leg rope slings, the Working Load Limit of each leg will have to be reduced considerably. Consult industry recommendations for information such as published by the Cordage institute. Working Load Limit does not apply if rope has been subjected to severe dynamic loading, which may not be visible.
Avoid overheating
Exposure to high temperatures will cause ropes to lose strength rapidly. Even temperatures as low as 150⁰ F (66⁰ C) can reduce the strength of some ropes by 50%. When using synthetic rope (especially polypropylene) on a capstan or a winch, be careful to avoid excessive friction which heats, melts and fuses the outer fibers of the rope. Avoid repeated surging or hard rendering around poles or over cross arms. Polyester rope resists overheating best because its melting point is highest.
Attachments must have at least the same Working Load Limit as the rope used.
Hooks, links, shackles, etc. must be of suitable material and strength to provide adequate safety protection. Splice rope properly and use thimbles if applicable. Choose rope to match gear or gear to match rope. Sheaves, pulleys, thimbles, etc. that do not match the size of rope being used can cause dangerous friction, abrasion, overload, etc.
Keep out from under a raised load.
Do not move load over people. Do not ride on load. Conduct all lifting operations in such a manner that if equipment were to fail or break, no personnel would be injured. This means KEEP OUT FROM UNDER A RAISED LOAD, DO NOT OPERATE LOADS OVER PEOPLE AND KEEP OUT OF THE LINE OF FORCE.
Avoid Shock loads.
Rope that is strong enough to withstand a steady pull can be broken with a sudden jerk. Be aware of all possible dynamic loading situations. Avoid them when possible and allow for strong enough rope when they cannot be avoided. Keep in mind that the effects of dynamic loading are greater on shorter ropes than on longer ones and greater on low elongation ropes (such as Manila and polypropylene) than on high elongation rope (such as nylon). Never stand in the line of rope under strain. If the rope breaks it will recoil with considerable force, especially if it is nylon.
Inspect rope frequently.
Closely examine entire length of rope for damage to determine general condition and detect localized wear. Excessive abrasion, fusing of outside fibers, hockles, rust or other chemical stains, broken fiber or other obvious damage to rope are reasons to retire rope from service. Internal damage can be assessed by twisting strands open and checking for powdered fiber. Rope that is suspected of having been exposed to severe shock loads or loads close to its catalog Breaking Strength should be retired immediately. Such damage may not be visible. Actual remaining strength of damages or used rope can only be established by laboratory analysis and tension tests.
Destroy, rather than discard, rope to be retired.
It might be used again by someone not aware of the hazard or defect. This is best achieved by cutting it up into short pieces.
Rope slings.
Refer to OSHA standard 1910.184 and ASME standard B30.9 for design factors and other important information. Other standards and information may apply in specific applications.
Refer to “Proper Care of Rope” for additional important cautions.
PROPER CARE OF ROPE
Avoid abrasion and unnecessary wear. Outer fibers as well as inner fibers contribute to a rope’s strength. When outer fibers are worn by chafing or dragging over splintered, rough or gritty surfaces, the rope is worn and weakened, When rope is used on cleats, winchheads, etc. make sure they are smooth and use chafing gear if necessary.
Avoid sharp angles and bends. Sharp angles greatly affect the strength of a rope. Any sharp angles or bend is a weak spot. Use thimbles or chafing gear or padding where possible. Knots are also weak spots. They can reduce strength by as much as 50% or more. Use splices instead. Splice rope correctly. When a small section of a rope has been worn or damaged, cut out the section and splice it together. Splice in extra trucks for synthetic fiber ropes. Use proper splicing procedures as outlined by the Cordage Institute. Do not resplice rope that broke due to being overloaded – discard it instead. Its remaining strength will only be a fraction of the Working Load Limit When new. Prevent unraveling of rope – whip to tape cut ends.
Avoid sustained loads. Fiber ropes subjected to heavy loads for long periods of time can break well below catalog Breaking Strength. Natural fiber ropes such as Manila and Sisal have less ability to take sustained loads synthetic fiber ropes such as nylon or polypropylene. Never exceed the Working Load Limit and do not subject fiber rope to sustained loads for more than two days.
Avoid rust. All ropes, synthetic or natural, should be kept away from rusting iron or steel. Rust can cause rapid loss of strength, sometimes in as short a time as one to two weeks. If ropes become rust stained, inspect the extent of the stain. If it is halfway through the rope, then rope strength may be reduced by as much as 50%.
Keep rope away from chemicals. Even though synthetic rope is generally considered to be resistant to damage from oils, gasoline, paint and most chemicals, exposure to any of these may cause some damage. Avoid contact with such things as storage battery solution, washing compounds or solution, and animal wastes. Strong acids, alkalis and solvents can damage any rope. Natural fiber rope is extremely vulnerable to all chemicals and solvents.
Avoid the use of swivels in ropes under load – a loss of turn will cause permanent damage to the rope.
Never use a nylon line which has a high stretch factor in combination with another rope of low stretch. The nylon line will stretch and not carry its proportionate share of the load, thus putting extra strain on the other lines.
Reverse ends of the rope periodically. Especially in tackles and winches, reverse the rope end-for-end periodically so that all sections will be worn equally. Also, using a line in one direction over a winch many times can also damage the rope by twisting it too tight or untwisting it so that hockles occur. Kinks pulled through a restricted space such as a tackle block, can seriously damage rope fibers. The initial use should be in a clockwise direction, then reverse the rope periodically.
Slack off guys in wet weather. When rope are used as guy lines or other supports exposed to weather, they should be slacked off in wet weather, or damage to the rope, as well as what it is supporting, may result.
Store rope properly. Rope is best stored in a dry, unheated place where air circulates freely, off the floor, and away from direct sunlight and other contact with the elements. Keep in mind that synthetic ropes will deteriorate in direct sunlight due to exposure to ultraviolet radiation. Light colored polypropylene especially is severely affected, smaller diameters more so than large sizes. Natural fiber ropes (Manila and Sisal) will deteriorate in storage even under ideal conditions.
Dry rope properly. Whenever natural fiber ropes become wet they should always be thoroughly dried before they are stored or they will rot in a very short time. Do Not dry synthetic fiber rope in direct sunlight.
Keep rope clean. Dirt on the surface of the rope can become embedded inside and act as an abrasive on fibers. When rope gets dirty, wash it thoroughly with clean fresh water. Remember to dry natural fiber rope before storing.
Remove rope from coils and reels properly. Regular right hand laid rope should be uncoiled in a counter clockwise direction.
Coiled rope: Lay the coil on the floor with the inside end at the bottom, then reach down though the center and pull the inside up through the coil.
Reeled rope: Remove the rope from a reel by pulling it off the top while the reel is free to rotate. Rope should never be taken from a reel lying on its end because it is more likely to kink or hockle or pull yarns on the wooden flange.
When substituting natural fiber rope with synthetic fiber ropes (or substituting one synthetic rope for another) substitution should not be made on a straight breaking strength –for-breaking strength basis only. Other important factors must be considered.